Floor resins
The suggested application fields of EPOREZIT construction
industrial systems: concrete correction, filling of cracks,
gaps, joints, impregnation, base, coating of concrete, corrosion
protection of fixtures, industrial and decorative floor coverings,
production of stairs, columns, artificial stone, artificial marble
pieces from epoxy concrete, gluing of old and new concrete or concrete
and metal.
Detailed information.
In case You need further information on our EPOREZIT construction
industrial systems, please contact our representative Contact
|
EPOREZIT Resin |
EU-sign |
EPOREZIT hardener |
EU-sign |
Mixture ratio |
Main Applications |
Pot life |
Bonding time |
Hardness, |
|||||
|
"A" |
|
|
"B" |
|
|
A : B |
|
min |
h |
24 h |
48 h |
72 h |
7 nap |
|
EB-43 |
|
|
T-43 N |
|
|
3 : 1 |
Material of case coatings, coating, epoxy mortars and coatings, high filled mortars. |
52 |
24 |
40 |
45 |
67 |
67 |
|
EB-43 |
|
|
T-43 S |
|
|
7 : 3 |
Material of case coatings, coating, epoxy mortars and coatings, high filled mortars. |
19 |
24 |
55 |
65 |
65 |
65 |
|
EB-47 |
|
|
T-47 |
|
|
3 : 1 |
Material of case coatings, coating, epoxy mortars and coatings, high filled mortars. Stone carpet, decorative coating |
20 |
24 |
55 |
65 |
72 |
72 |
|
EB-48 |
|
|
T-48 |
|
|
2 : 1 |
Material of case coatings, coating, epoxy mortars and coatings, high filled mortars. |
40 |
24 |
35 |
55 |
65 |
65 |
|
RB 2 |
|
|
T-3 |
|
|
100 : 10 |
Concrete correction, impregnation, base coating |
20 |
24 |
- |
- |
- |
- |
|
RB 2 |
|
|
T-30 |
|
|
100 : 20 |
With a high amount of filling material for the production of decor stairs, artificial stone, artificial marble. Recommended temperature of processing: above +10 °C |
32 |
24 |
20 |
52 |
52 |
52 |
|
RB 2 |
|
|
T-54 |
|
|
100 : 40 |
Concrete correction, base coating. Recommended temperature of processing: above +10 °C |
25 |
24 |
55 |
60 |
62 |
69 |
|
EB-52 |
|
|
T-52 |
|
|
5 : 1 |
Colored, self-leveling flooring system, decor floor, top coats. |
60 |
24 |
55 |
65 |
75 |
75 |
|
EB-53 |
|
|
T-53 |
|
|
4 : 1 |
Colored, self-leveling flooring system, decor floor, top coats. |
40 |
24 |
45 |
60 |
70 |
75 |
|
AKVA 100 A |
|
|
AKVA 100 B |
|
|
1 : 3 |
Filled, waterborne coating |
155 |
24 |
19 |
49 |
49 |
49 |
|
AKVA 100 A |
|
|
T-100 |
|
|
100 : 110 |
Waterborne base coating |
60 |
24 |
|
|
|
|
|
AKVA 100 A |
|
|
T-500 |
|
|
100 : 90 |
Waterborne base coating |
60 |
24 |
|
|
|
|
|
KOTERM A |
|
|
KOTERM B |
|
|
100 : 10 |
ca. 35 |
24 |
- |
- |
- |
- |
|
|
|
Irritant |
|
Dangerous for the environment |
|
Corrosive |
|
Flammable |
It makes the surface of the concrete dust-free and easy to clean. It forms a waterproof layer on the surface of the concrete. The transparent covering gives back the appearance of concrete. The covering is shiny. We recommend our EPOREZIT EB-47/T-47 or EPOREZIT EB-43/T-43 system for dust removal coatings. Before applying the layers, the surface has to be treated adequately. The surface to be covered should be dry and free of loose particles, dust, oily and greasy pollutions.
|
Layers |
|
EPOREZIT resin |
EPOREZIT cross-linking agent |
Mixture ratio (mass based) |
Material need |
Equipment |
Remark |
|
|
|
„A” |
„B” |
A : B |
kg/m2 |
|
|
|
1. |
Base coating |
EB-47 |
T-47 |
3:1 |
0,3-0,4 |
Rubber squeegee / paint roller |
It is absorbed into the surface of the concrete. |
|
2. |
Covering |
EB-47 |
T-47 |
3:1 |
0,2-0,3 |
Rubber squeegee / paint roller |
Application within 24 hours after layer 1 is cross-linked |
|
|
|
|
|
Altogether |
0,5-0,7 |
|
|
It makes the surface of the concrete
dust-free, non-skid and easy to clean. It forms a waterproof layer on
the surface of the concrete.
The covering is shiny, the extent of non-skid depends on the grain size
of the fire-baked silica sand applied.
The covering layer can be our transparent EPOREZIT EB-47/T-47 or
EPOREZIT EB-43/T-43 system, or EB-52/T-52 or EPOREZIT EB-53/T-53 system
in the desired RAL color - as demanded
Before applying the layers, the surface has to be treated adequately.
The surface to be covered should be dry and free of loose particles,
dust, oily and greasy pollutions
|
Layers |
|
EPOREZIT resin |
EPOREZIT cross-linking agent |
Mixture ratio (mass based) |
Material need |
Equipment |
Remark |
|
|
|
„A” |
„B” |
A : B |
kg/m2 |
|
|
|
1. |
Base coating |
EB-47 |
T-47 |
3:1 |
0,3-0,4 |
Rubber squeegee / paint roller |
It is absorbed into the surface of the concrete. |
|
2. |
Correction of the surface at the necessary places |
EB-47 |
T-47 |
3:1 |
Resin mix filled with 50-70 weight % silica sand |
Float |
Correction of the surface if necessary (in case of cracks, gaps, holes) |
|
3. |
Base coating |
EB-47 |
T-47 |
3:1 |
0,2-0,3 |
Rubber squeegee / paint roller |
Application within 24 hours after layer 1 is cross-linked |
|
4. |
Sanding (fire-baked silica sand) |
|
|
|
2,5-3 |
|
After applying layer 3 but before it cross-links. |
|
5. |
Covering |
EB-47 |
T-47 |
3:1 |
0,3-0,4 |
Rubber squeegee / paint roller |
After applying layer 4 and removing the surplus sand |
|
|
|
|
Altogether |
EB-47/T-47 |
0,8-1,1 |
|
|
|
|
|
|
|
Silica sand |
2,5-3 |
|
20-30 % can be gained back after step 4 |
It makes the surface of the concrete
dust-free and easy to clean. It forms a waterproof layer on the surface
of the concrete.
The covering is shiny, and has the desired color. The covering layer is
our EB-52/T-52 or EPOREZIT EB-53/T-53 system in the desired RAL color -
as demanded. Chips decor can be applied as layer 6.
Before applying the layers, the surface has to be treated adequately.
The surface to be covered should be dry and free of loose particles,
dust, oily and greasy pollutions.
|
Layers |
|
EPOREZIT resin |
EPOREZIT cross-linking agent |
Mixture ratio (mass based) |
Material need |
Equipment |
Remark |
|
|
|
„A” |
„B” |
A : B |
kg/m2 |
|
|
|
1. |
Base coating |
EB-47 |
T-47 |
3:1 |
0,3-0,4 |
Rubber squeegee / paint roller |
It is absorbed into the surface of the concrete. |
|
2. |
Correction of the surface at the necessary places |
EB-47 |
T-47 |
3:1 |
Resin mix filled with 50-70 weight % silica sand |
Float |
Correction of the surface if necessary (in case of cracks, gaps, holes). |
|
3. |
Base coating |
EB-47 |
T-47 |
3:1 |
0,2-0,3 |
Rubber squeegee / paint roller |
Application within 24 hours after layer 1 is cross-linked. |
|
4. |
Covering |
EB-52 |
T-52 |
5:1 |
0,5-0,6 |
Rubber squeegee / rack |
Application within 24 hours after layer 3 is cross-linked. |
|
5. |
Covering |
EB-52 |
T-52 |
5:1 |
0,4-0,5 |
Rubber squeegee / rack |
Application within 24 hours after layer 4 is cross-linked. |
|
6. |
Chips decor |
|
|
|
|
spraying |
Application after spreading layer 5, before its cross-linking. |
|
|
|
|
Altogether |
EB-47/T-47 |
0,5-0,7 kg/m2 |
|
|
|
|
|
|
|
EB-52/T-52 |
0,9-1,1 kg/m2 |
|
|
It is a decorative, natural like covering of
aesthetic appearance
It makes the surface of the concrete dust-free and easy to clean. It
forms a waterproof layer on the surface of the concrete
The surface of the coating is shiny or dull, based on the covering
layer.
Before applying the layers, the surface has to be treated adequately.
The surface to be covered should be dry and free of loose particles,
dust, oily and greasy pollutions
|
Layers |
|
EPOREZIT resin |
EPOREZIT cross-linking agent |
Mixture ratio (mass based) |
Material need |
Equipment |
Remark |
|
|
|
„A” |
„B” |
A : B |
kg/m2 |
|
|
|
1. |
Base coating |
EB-47 |
T-47 |
3:1 |
0,3-0,4 |
Rubber squeegee / paint roller |
It is absorbed into the surface of the concrete |
|
2. |
Silica sand |
|
|
|
|
|
Scattering until layer 1 is cross- linked |
|
3. |
Binding agent |
EB-47 |
T-47 |
3:1 |
|
|
|
|
|
Silica sand / resin |
|
|
|
4-6 |
Float |
3-4 mm floor |
|
|
Silica sand / resin |
|
|
|
8-10 |
Float |
6-8 mm floor |
|
|
Silica sand / resin |
|
|
|
12-14 |
Float |
10 mm floor |
|
4. |
Covering |
EB-47 |
T-47 |
3:1 |
0,3-0,4 |
Rubber squeegee / paint roller |
Absorbed into the gaps |
|
5. |
Covering |
EB-47 |
T-47 |
3:1 |
0,2-0,3 |
Rubber squeegee / paint roller |
Provides a shiny surface |
|
|
|
|
Altogether |
EB-47/T-47 |
0,8-1,1 kg/m2 |
|
|
|
|
|
|
|
Silica sand/resin mix |
Depending on layer thickness |
|
|
The filled, colored thin aqueous epoxy floor
covering makes the surface of the concrete dust-free and easy to clean.
It forms a waterproof layer on the surface of the concrete but it is
vapor- permeable. It prevents the absorption of harmful materials into
the concrete
The surface of the coating is dull, it gives back the pattern of the
surface of the concrete. It is environment-friendly, can be diluted
with water.
Before applying the layers, the surface has to be treated adequately.
The surface to be covered should be dry and free of loose particles,
dust, oily and greasy pollutions
|
Layers |
|
EPOREZIT resin |
EPOREZIT cross-linking agent |
Mixture ratio (mass based) |
Material need |
Equipment |
Remark |
|
|
|
„A” |
„B” |
A : B |
kg/m2 |
|
|
|
1. |
Base coating |
AKVA 100 „A” |
AKVA 100 „B” |
1:3 |
0,4-0,5 |
Rubber squeegee / paint roller |
Diluted with max. 15 % water |
|
2. |
Intermediate layer |
AKVA 100 „A” |
AKVA 100 „B” |
1:3 |
0,3-0,4 |
Rubber squeegee / paint roller |
Diluted with max. 3 % water |
|
3. |
Covering |
AKVA 100 „A” |
AKVA 100 „B” |
1:3 |
0,2-0,3 |
Rubber squeegee / paint roller |
Without dilution |
|
|
|
|
Altogether |
AKVA 100 „A”/ AKVA 100 „B” |
0,9-1,2 kg/m2 |
|
|